Characteristic & main applications Universal high-pressure gasket suitable for use in a wide range of applications with good stress relaxation. Suitable for hot water, steam, oil, hydrocarbons and many other chemicals.
Material Aramid fibre bonded with NBR.
pT diagram
The Klinger pT diagram provides guidelines for determining the suitability of a particular gasket material for a specific application based on the operating temperature and pressure only. Always refer to the chemical resistance of the gasket to the fluid.
Technical Data
Typical values for 2 mm thickness
Compressibility ASTM F 36 J
%
14
Recovery ASTM F 36 J
min.
%
50
Stress relaxation DIN 52913
50 MPa, 16 h/300 °C
MPa
20
50 MPa, 16 h/175 °C
MPa
24
Stress relaxation BS 7531
MPa
-
Klinger cold/hot compression 50 MPa
thickness decrease at 23 °C
%
10
thickness decrease at 300 °C
%
25
Tightness according DIN 3535/6
ml/min
0,2
Thickness increase after fluid immersion ASTM F 146